Gelcasting相关论文
Microstructure and properties of porous Si3N4 ceramics by gelcasting-self-propagating high-temperatu
Porous silicon nitride ceramics have attracted a considerable attention due to their excellent overall performance,but p......
Frequent offshore oil spill accidents, industrial oily sewage, and the indiscriminate disposal of urban oily sewage have......
Porous Ti compacts with large size and complex shape for biomedical applications were fabricated in the porosity range f......
...
以α-Al2 O3、金红石型TiO2和MgO为初始粉料，采用凝胶注模成形工艺制备了Al2（1－x）MgxTi1＋xO5固溶体陶瓷。将陶瓷试样浸泡到750℃的铝熔......
Spherical Ti-45Al-8.5Nb-(W,B,Y)alloy powder prepared by an argon plasma process was near-net shape by gelcasting.In the ......
An approach to fabricate sintered copper with high green strength and high sintered density using nonaqueous gelcasting ......
The influence of dispersants and decentralization condition on rheological properties and gelcasting of BNA12O3-Y2 O3 sl......
The raw materials of Al, Si, SiO2, and SiC were used to prepare Sialon-SiC suspension for gelcasting by adjusting the pH......
A novel near-net process, gelcasting, was successfully used to prepare larger size 316L stainless steel parts with compl......
Bipolar plate is one key component of proton exchange membrane fuel cell (PEMFC). According to this paper, mesocarbon mi......
研究了分散剂以及浆料固相体积分数对刚玉-尖晶石浆料粘度的影响,并研究了单体质量分数、催化剂、引发剂加入量对刚玉-尖晶石体系......
对用于凝胶注模成型的氧化铝悬浮液进行了分散效果和流变性的研究.根据液体介质中分散固体颗粒的三种基本分散机制,通过调节悬浮液......
对凝胶注模成型氧化铝的具体工艺参数进行了初步的研究,包括单体用量、单体与交联剂的比例、引发剂的用量和固相含量等参数对凝胶......
研究了研磨时间、分散剂掺量、固含量对Al2O3-TiO2料浆流变性能的影响。研究结果表明，当研磨时间为4h，分散剂掺量为3％（mass fraction o......
激光加工陶瓷坯体的工艺，可以使陶瓷的加工更加接近于金属的加工过程。该工艺首先通过先进的陶瓷成型技术制备出高度均匀的陶瓷坯体......
Sintering additives to gelcasting Sialon-SiC were decided by the optimizing experiments.The results show that Soalon-SiC......
采用凝胶注模成型技术制备ZnO陶瓷坯体,并在较低温度下常压烧结后获得相对密度达98.6%、晶粒尺寸为1.35μm的陶瓷靶材,研究工艺参......
探讨了陶瓷凝胶注模成型的机理和特点,研究了固相体积含量、pH值、分散剂等对制备低粘度、高固相体积含量的氧化铝陶瓷悬浮液的影......
研究了ZTA陶瓷注凝成型浆料流变性能的影响因素.结果表明:单体(AM)在液相中质量百分浓度为10%、交联剂与单体的比(MBAM/AM)较低时,......
本文研究了BaTiO3基PTC陶瓷的凝胶注模成型工艺,包括浆料的制备,交联剂的用量,引发剂和催化剂用量及环境温度对可操作时间的影响规......
讨论固相含量高达５０ｖｏｌ％的ＳｉＣ水基悬浮体的制备和凝胶注模成型。ＳｉＣ粉末适于在碱性水溶液中分散，但溶液的ＰＨ值必须适当。ＳｉＣ料浆的流变性同时受球 固......
目的为了实现低成本、低能耗、高效率制备大尺寸复杂形状钛合金的问题,以凝胶注模技术为成形手段,制备近净成形Ti6Al4V合金,并研究......
采用硅溶胶分散氧化铝浆料免脱气注凝成型工艺，利用硅溶胶凝胶化在氧化铝颗粒表面原位形成纳米SiO2包覆Al2O3微复合结构．实现莫来石......
多晶半透明氧化铝陶瓷作为高压钠灯灯管和各种窗体材料等已在实际生产中得到广泛应用。但由于其强度低、耐腐蚀和透光性差无法满足......
针对Al/SiCP复合材料机加工困难的问题,首先采用凝胶注模法得到具有复杂形状的SiCP预制块,再通过真空压力浸渗近净成形制备具有高S......
介绍一种新的陶瓷成型技术－－凝胶注模成型，它是在陶瓷浆料中加入有机单体浇铸后，在一定的条件下，有机单体发生原位聚合反应，使陶瓷浆料凝......
The raw materials of Al, Si, SiO2, and SiC were used to prepare Sialon-SiC suspension for gelcasting by adjusting the pH......
70v01．％-78v01．％的sialon．sic悬浮体在10-160S-1范围内显示剪切变稀的幂率特征，突出的“切稀”行为满足凝胶注模成型的要求。建立的悬浮......
本文介绍近年来发展起来的陶瓷材料成形的铸技术。讨论了凝胶铸成形的工艺条件、影响因素,并对该技术的应用及发展前景进行了分析......
研究了分散剂的种类、用量、料浆pH值、球磨时间、有机单体含量等因素对氧化硅料浆性能的影响,制备出固相体积分数达42vol%,流变性......
采用凝胶注模技术原位合成造孔剂制备出开孔气孔率为20%～30%的La0 8Sr0.2MnO3多孔阴极材料.结果表明,合适的烧结温度为1 100℃～l150......
研究了采用新体系的陶瓷悬浮体的分散性、流变行为、固化特性以及坯体的抗弯强度。...
在对氮化硅粉进行助烧剂包覆和凝胶注模成型的基础上，研究了冷等静压凝胶注膜成型氮化硅坯体。氧化氮化硅包覆料和气压烧结制度对凝......
用无机盐共沉淀法在氮化硅颗粒表面包覆一层纳米级的钇铝氧化物后，粉料的分散性大大提高，可用来制备固相体积分数为50%的悬浮体，利用......
研究了分散剂用量、固相体积含量对碳化硼浆料粘度的影响,采用扫描电子显微镜(SEM)对素坯微观结构进行了表征。结果表明,以正辛醇......
传统方法制备高性能炭素和石墨材料是一个高能耗的漫长过程。本文首次对高性能石墨材料进行注凝成型工艺研究,讨论了分散剂含量、p......
提出了一种移动通信用的介质滤波器的结构和设计方法，采用以Ba5-3x（Srn1-yNdy）s＋2xTi18O54为基的微波介质陶瓷材料，并将凝胶注模成型（Gel......
为制备凝胶注模成型所需的高固相低粘度的锆钛酸铅陶瓷浆料，分别用分散剂聚甲基丙烯酸铵和柠檬酸三铵进行试验．研究了分散剂聚甲基丙......
该文利用凝胶注模工艺和无压浸渗技术相结合的方式,首先利用凝胶注模工艺制备碳化硅预制体,然后利用无压浸渗工艺制备颗粒直径为40......
选用Al2O3粉体和单体为N-羟甲基丙烯酰胺（NMA）的聚合体系配成浆料,结合凝胶注模和离心成型工艺的优点,制备出直径分别为12、18、30 m......
采用不同雕刻工艺参数对凝胶注模成型的Al2O3陶瓷坯体进行雕刻试验。详细分析了工艺参数对单层雕刻深度、雕刻质量的影响以及激光......
以板状刚玉和富铝尖晶石为主原料，采用泡沫浸浆凝胶工艺制备了Al2O3-(30 vol％)MgO·1．35Al2O3泡沫陶瓷。研究了分散剂AN-2000与pH......
以Al粉、Si粉、SiO2微粉和粗细两种粒度的SiC为原料，利用凝胶注模成型技术制备了SiAlON与SiC的质量比为1：3的SiAlON-SiC材料，研究了其......
以板状刚玉颗粒和富铝尖晶石细粉为主要原料，以含丙烯酰胺(AM)、N，N-亚甲基双丙烯酰胺(MBAM)和分散剂AN-2000的水溶液为预混液，制备出......
采用快速成型和快速模具技术制备了具有复杂结构的模具．采用凝胶注模成型工艺成功制备出固相体积百分数含量为55，粘度小于1Pa·s......
本文研究了ＺｒＯ２（３Ｙ）－Ａｌ２Ｏ３复相陶瓷的凝胶注模成形工艺，着重研究了低粘度高固相体积分数浓悬浮体的制备。......
采用自主开发的非水基凝胶注模工艺,对高速钢粉末进行了凝胶注模的研究。所开发的非水基凝胶注模体系能够为金属粉末的成形开辟一......
采用凝胶注模成形工艺制备Fe-Cu-C合金，研究了该合金体系中不同固相体积分数对凝胶注模干燥速率和干燥收缩的影响，以及不同粒度所能......
以自由基聚合反应动力学原理为基础，研究中间相炭微球水基浆料凝胶反应动力学。考察了引发剂用量、催化剂用量、模具温度和单体浓度......